Technical ASTM F593 Abstract
Page 1 of  2          1   2   Chemical Requirments Alloy Group Alloy Composition, percent maximum except as shown C Mn P S Si Cr Ni Cu Mo Other Austenitic Alloys 1   303 303Se 304 305 384 XM1 XM7  0.15 0.15 0.08 0.12 0.08 0.08 0.  2.00 2.00 2.00 2.00 2.00 5.0-6.5  0.20 0.02 0.045 0.045 0.045 0.040  0.15min 0.060 0.030 0.030 0.030 .18  1.00 1.00 1.00 1.00 1.00 1.00 1.  17.0-19.0 17.0-19.0 18.0-20.0 17.0-19.0  8.0-10.0 8.0-10.0 8.0-10.5 10.5-13.0 1  1.75-2.2 3.00-4.0  0.60 max  Se 0.15  Austenitic Alloys 2   316  0.08  2.00  0.045  0.030  1.00  16.0-18.0  10.0-14.0    2.00-3.0    Austenitic Alloys 3   321 347  0.08 0.08  2.00 2.00  0.045 0.045  0.030 0.030  1.00 1.00  17.0-19.0 17.0-19.0  9.0-12.0 9.0-13.0      Ti 5 X C min Cb +Ta 10 X C min  Ferritic Alloys 4   430 430F  0.12 0.12  1.00 1.25  0.040 0.060  0.030 0.15 min  1.00 1.00  16.0-18.0 16.0-18.0      0.60max    Martensitic Alloys 5   410 416 416Se  0.15 0.15 0.15   1.00 1.25 1.25  0.040 0.060 0.060  0.030 0.15min 0.060  1.00 1.00 1.00  11.5-13.5 12.0-14.0 12.0-14.0      0.60max  Se 0.15  6   431  0.20  1.00  0.040  0.030  1.00  15.0-17.0  1.25-2.50        Precipitation Hardening Alloys 7   630  0.07  1.00  0.040  0.030  1.00  15.5-17.5  3.00-5.00  3.00-5.00    Cb + Ta 0.15-0.4